I. Introduction
Diseases affecting the brain and the central nervous system (Alzheimer’s, Parkinson’s) are among those with the greatest impact on our society. Prevention and early diagnosis are very effective, but the equipment and procedures employed are currently too expensive for general application. The European ENIAC JU project CSI aims to advance the state of the art in three-dimensional (3D) medical-imaging platforms to improve the efficiency of the diagnosis and therapy of these serious diseases.

II. Challenges and methods
Nowadays, specific issues arise with the temperature and stress sensitivity of detector devices. During the assembly process the components already suffer from a stress cycle that appears during the soldering process. The present lead-free solder is, compared to the former eutectic solder not very compliant, in the sense of stress relaxation. For that purpose work on low temperature interconnect processes is needed.

An investigation has been carried out for low temperature alloys which may be used for TSV interconnect. A list of candidate alloys has been established. These alloys are obviously lead-free alloys that consist of the following elements: Indium, Bismuth, Tin, Zinc and Silver. The lowest melting temperature is 70°C and the highest is 140°C. During further research various physical and mechanical properties of these alloys, i.e. melting temperature (eutectic alloys) or melting temperature range, electrical conductivity, thermal conductivity, thermal coefficient of expansion, elongation, shear strength, creep behavior, hardness, wettability, latent heat of fusion and specific heat solid/liquid will be investigated.

III. Low melting alloys
To achieve a low stress SiPM (Silicon Photomultiplier), low melting alloys are desired for soldering of SiPM on PCB. Indium (In) based alloys are the main group of the candidate low meting solders. However the mechanical properties of high In alloys are inferior. Adding other elements like Ag, Zn and Sn could cause a stronger alloy. Nine solders with a melting temperature and/or melting range between 70ºC and 140ºC have been selected for this study. Microstructure of these low melting solder alloys has been investigated.

IV. Mechanical behavior of low melting alloys
Nine different low melting solder alloys were made in a controlled atmosphere with less than 1 ppm oxygen pressure. The nine different low melting solder alloys were casted in a mold with dimensions: 28×22 mm. The thickness of the casted solder was approximately 4 mm. Subsequently, the casted solder was cold rolled . Mechanical behavior and microstructure were qualified.

Solder alloy MT-100640 (In57Sn17Bi26) (a) SEM picture of microstructure at enlargement 1000x (b) alloy cold rolled until cracked (20% thickness reduction).

V. Conclusions
In the first year’s framework of the CSI project, various low melting solder alloys were made. The microstructure and mechanical behavior of the solder alloys were studied by cold rolling. Amongst others, the following conclusion can be drawn from this investigation:

  • Solder alloys MT-100508 (In78,5Bi21,5), MT-100625 (In52,2Bi46Zn1,8), MT-100289 (In51Sn49) show a relatively soft character regarding the mechanical behavior during cold rolling.
  • Solder alloy MT-100511 (In51.2Sn45Zn1.8Ag1.5) shows a promising mediate character regarding the mechanical behavior during cold rolling.
  • Solder alloy MT-100640 (In57Bi26Sn17), MT-100509 (In50Bi50), MT-100504 (Sn47Bi47In5Ag1), MT-100505 (Sn47Bi47In5Ag2) and MT-100506 (Sn47Bi47In5Ag3) show a relatively brittle character regarding the mechanical behavior during cold rolling.

VI. Future work

  • Determining of melting point or range of the solder alloys.
  • Determining mechanical properties by applying required experiments.
  • Further alloying of In-based alloys to achieve the desired mechanical properties.

VI. Author
M. Biglari. Participates in project CSI (ENIAC): ST Microelectronics-Italy (Italy), University of Bologna (Italy), Politecnico of Torino (Italy), Philips (The Netherlands), IMEC-NL (The Netherlands), Kempenhaeghe (The Netherlands), Mat-Tech (The Netherlands), AMS (Austria), GTech (Austria), AIT (Austria), Institute of Nuclear Research ATOMKI (Hungary), Mediso (Hungary), University of Debrecen (Hungary), University of Pannonia (Hungary).

Download the pdf file here.

Knowledge Centre

Mat-tech closely follows international developments in the field of high-tech brazing. The Development & Testing Department has access to new and fundamental research in the field, and is also actively involved in a number of international projects. The knowledge that Mat-tech acquires is shared with our clients, industry peers and other parties where there is a common ground in high-tech brazing.

We are actively sharing our knowledge at fairs, seminars and on this platform as well as other media.

Read more

Membership & Certificates

Mat-tech is a member of various national and international (branch) organizations, namely:

©2021 Mat-tech BV