I. Introduction II. Specification of the industrial problem Fig. 1: Optical images (“top view”) of the initial Ti-6Al-4V alloy parts. III. Direct low-pressure diffusion bonding

ABSTRACT Successful brazing of any Aluminium alloy requires prior removal of the native surface oxide film,which is usually done by employing a flux. Magnesium additions

ABSTRACT Brazing of several refractory metals, namely, Tungsten, Molybdenum and Niobium as wellas austenitic stainless steel AISI 304 to pure Copper was performed in vacuum

I. Specification of the problem The present Project is dealing with the fabrication of electrical (high-voltage) feedthrough consisting of YSZ (ZrO2 + 3 % mole

I. Introduction Aluminium Oxide Ceramics due primarily to its good heat conductivity (of about 30 W×m-1×K-1) and a relatively low cost is considered as an

I. Introduction Our previous investigation of the interfacial regions in the ”(p-n) thermocouple” / Cu- connector assembly (Project No. 2012-3067-0616) was aimed at providing a